경북대 / 김홍주*
Abstract
New single crystal of Ce-doped Tl2LiGdBr6 (TLGB) was investigated under x-ray and γ-ray excitation. Two zone vertical Bridgman technique was used to grow this scintillation material. Under X-ray excitation, typical Ce3+ ion emission was observed between 397 and 456 nm peaking at 422 nm. An energy resolution of 17% (FWHM) and 17,400 ± 1700 ph/MeV light yield was obtained for 662 keV γ-rays excitation. Under γ-rays excitation from a 137Cs source, two decay time components of 29 ns (92%) and 197 ns (8%) were found at room temperature. Further investigation is underway for the optimization of the Ce-concentration in the host lattice. We expect improvement in the scintillation properties with a good quality crystal of this material.
Highlights
•Scintillation properties of new Tl-based alkali halide eplasolite activated by Ce3+ are presented.
•This material is grown by two zone vertical Bridgman technique.
•It possessed high Z-number, high density, fast decay component and moderate light yield.
•Further improvements in the crystal quality could make this scintillator best choice for the use in medical imaging.
Author information
H.J. Kima, Gul Roohb, H. Parka, Sunghwan Kimc
a Department of Physics, Kyungpook National University, Daegu 702-701, South Korea
b Department of Physics, Abdul Wali Khan University, Mardan 23200, Pakistan
c Department of Radiological Science, Cheongju University, Cheongju 360-764, South Korea